Effect of post-annealing on the photocatalytic activity of hydrothermally synthesised titania nanotubes

Wadhwa, S, Hamilton, JWJ, Dunlop, PSM, Dickinson, C and Byrne, JA (2011) Effect of post-annealing on the photocatalytic activity of hydrothermally synthesised titania nanotubes. Journal of Advanced Oxidation Technologies, 14 (1). pp. 147-157. [Journal article]

[img] PDF - Accepted Version
Indefinitely restricted to Repository staff only.



Heterogeneous photocatalysis has been reported to be effective for the degradation of a wide range of organic pollutants and the inactivation of pathogens in water. The use of nanostructured materials is one approach to improving photocatalytic efficiency. Titanate nanotubes were prepared by a hydrothermal synthesis and annealing yielded titania nanotubes, nanorods and crystals. These materials were characterized using XRD, XPS, BET and TEM. The photocatalytic activities were studied using phenol and formic acid as model pollutants. The as prepared titanate nanotubes had a very high specific surface area (401 m2g-1). Annealing at 400oC gave anatase TiO2, however, the tubular structure collapsed to rods leaving only 30% nanotubes. The sample containing 30% nanotubes was found to be 3.4 times more active than Degussa P25 for the photocatalytic oxidation of formic acid. Annealing at temperatures higher than 400oC caused a reduction in photocatalytic activity for the oxidation of formic acid. This correlated to a decrease in the specific surface area of the samples. In the case of phenol, the rate of photocatalytic oxidation increased with increasing annealing temperature, with the nanocrystals obtained at 700oC showing the highest rate, yet still lower than that observed for P25.

Item Type:Journal article
Faculties and Schools:Faculty of Computing & Engineering
Faculty of Computing & Engineering > School of Engineering
Research Institutes and Groups:Engineering Research Institute
Engineering Research Institute > Nanotechnology & Integrated BioEngineering Centre (NIBEC)
ID Code:17545
Deposited By: Dr Patrick Dunlop
Deposited On:22 Mar 2011 11:03
Last Modified:09 Dec 2015 10:55

Repository Staff Only: item control page