Savitskaya, TA, Epshtein, OL, Kulinkovich, OG and Tret'yakova, Svetlana (2000) Dynamic membranes based on poly(N-isopropylacrylamide-co-heptadecyl vinyl ketone): Preparation and properties. COLLOID JOURNAL, 62 (6). pp. 746-750. [Journal article]
Full text not available from this repository.
Dynamic membranes were prepared from poly(N-isopropylacrylamide-co-heptadecyl vinyl ketone) having a lower critical solution temperature in an aqueous solution and being a micelle-forming surfactant. The dependence of the critical concentration of the copolymer micellization an temperature was shown to have an extreme character with a minimum at the lower critical solution temperature of thr copolymer. The dynamic membranes are formed on both the hydrophilic (cellulose) and hydrophobic (polyacrylonitrile) supports. For the penetrants studied. it was found that the dynamic membrane formed on the hydrophobic support favors the rejection of a PEG(6000). while that formed on the hydrophilic support rejects more effectively albumin and sodium cellulose sulfoacetate. We failed to realize a completely reversible thermal control of transport properties of the dynamic membranes obtained, while it was readily accomplished for the membranes obtained by grafting N-isopropylamide onto a cellulose matrix.
|Item Type:||Journal article|
|Faculties and Schools:||Faculty of Art, Design and the Built Environment|
Faculty of Art, Design and the Built Environment > School of the Built Environment
|Research Institutes and Groups:||Built Environment Research Institute > Fire Safety and Engineering Research and Technology Centre (FireSERT)|
|Deposited By:||Dr Svetlana Tretsiakova-McNally|
|Deposited On:||16 Dec 2009 10:01|
|Last Modified:||10 Oct 2013 14:27|
Repository Staff Only: item control page